Product Description
| TYPES |
Plain, Flange, Double FLange, Thin Walled, Thick Walled
|
| MATERIAL |
BI-METAL, TRI-METAL, BABBITT METAL, BRONZE BACKED BABBITT METAL, AT, CAST ALUMINIUM
|
| USE |
Auto, Marine & Diesel Engines, Compressors, Turbines, Pumps
|
| GRADE |
SAE 792, SAE 794, SAE 49, SAE 12, SAE 15, SAE-783, SAE-770 ASTM Grade1, Grade2 Nickel Genuine, Grade13, Grade 15
|
| MFG PROCESS |
CLADDED OR SINTERED STRIP BEARINGS, CENTRIFUGAL CASTED
|
| FEATURES |
OE Quality, Easy To Fit, Custom Design and Sizes, Prompt Delivery
|
| OUTER DIAMETER |
20 mm to 300 mm
|
| LENGTH |
14 mm to 180 mm
|
| WALL THICKNESS |
1 mm to 23 mm
|
| Alloy Form | Lining Material | Metal Ref. | Brinell Hardness | Features And Applications |
|---|---|---|---|---|
| CAST BABBITT | LEAD BASED WHITE METAL | SAE-14 | 20 | THIS LEAD BASE BABBITT IS SOFT, EXCELLENT EMBED ABILITY FOR RELATIVE APPLICATIONS, MINIMUM LUBRICATION, GOOD RESISTANCE, LOW FATIGUE RESISTANCE AND HAS BEEN USED FOR MANY YEARS IN LOWER LOAD APPLICATION. |
| LEAD BASED WHITE METAL | SAE-15 | 18 | THIS LEAD BASE BABBITT HAS A GOOD BEARING PERFORMANCE, GOOD EMBED ABILITY AND HAS BEEN USED FOR MANY YEARS ON LOWER LOAD APPLICATION. | |
| TIN BASED WHITE METAL | SAE-12 | 32 | THIS TIN BASE BABBITT HAS GOOD SLIDING PROPERTIES, CONFORMABILITY AND HIGH TOUGHNESS; GOOD EMBED ABILITY SUITABLE FOR HIGH SLIDING VELOCITIES IN THE HYDRODYNAMIC RANGE, MEAN LOAD, IMPACT STRESS AT LOW FREQUENCY INSENSITIVE TO REVERSED BENDING STRESS. | |
| CAST COPPER LEAD | COPPER LEAD | SAE-793 | 80 | INCREASED HARDNESS AND WEAR RESISTANCE. INCREASING THE LEAD CONTENT IMPROVES THE TOLERANCE OF POOR ALIGNMENT AND INTERMITTENT LUBRICATION |
| COPPER LEAD | SAE-792 | 85 | THIS MATERIAL IS BEST SUITED FOR BUSHINGS AND WASHERS SUBJECTED TO HIGH IMPACT AND VIBRATORY LOADS. IN MOST CASES, IT OPERATES BEST WITH HARDENED SHAFT. | |
| COPPER LEAD | SAE-49 | 60 | HIGH FATIGUE STRENGTH, NORMALLY PLATED WITH AN OVERLAY WHEN USED IN BEARING APPLICATION AND IN THIS FORM MAY BE OPERATED WITH HARD OR SOFT SHAFTS SUSCEPTIBLE TO CORROSION BY DEGRADED OIL WHEN NOT OVERLAY PLATED | |
| COPPER LEAD | SAE-794 | 62 | HIGH FATIGUE STRENGTH AND SHOCK RESISTANCE, SUITABLE FOR HIGH SPEED SHAFTS, OSCILLATING OR ROTATING MOTION HARD SHAFT DESIRABLE, NORMALLY OVERLAY PLATED WHEN USED IN BEARING APPLICATION. | |
| SINTERED COPPER LEAD | COPPER LEAD | SAE-792 | 110 | THIS MATERIAL IS BEST SUITED FOR BUSHINGS AND WASHERS SUBJECTED TO HIGH IMPACT AND VIBRATORY LOADS. IN MOST CASES, IT OPERATES BEST WITH A HARDENED SHAFT. |
| COPPER LEAD | SAE-49 | 55 | THIS IS A BEARING MATERIAL DESIGNED EXCLUSIVELY FOR HIGH LOAD. THE MATERIAL IS PLATED WITH A UNIQUE TRI METAL OVERLAY AND NICKEL DAM. | |
| COPPER LEAD | SAE-794 | 50 | THIS MATERIAL IS EMPLOYED FOR BUSHINGS AND THRUST WASHERS APPLICATIONS SUBJECTED TO INTERMEDIATE IMPACTS AND VIBRATORY LOADS. IT HAS CERTAIN DEGREE OF EMBED ABILITY AND IT IS SUITABLE FOR HIGHER SPEED AND LOAD. | |
| CLAD ALUMINIUM | ALUMINIUM TIN | SAE-783 | 40 | THIS HAS GOOD FATIGUE RESISTANCE, GOOD SURFACE BEHAVIOR AND EXCELLENT CORROSION RESISTANCE TO WITH STAND INTERMEDIATE TO HEAVY LOAD OF MAIN ,CON ROD BEARING, THRUST WASHER AND WRAPPED BUSHES FOR HARD AND SOFT SHAFTS. |
| CAST ALUMINIUM (SOLID) | ALUMINIUM TIN | SAE-770 | 55 | - |
| OVERLAY PLATING | LEAD TIN | SAE-191 | 12 | - |
| LEAD TIN COPPER | SAE-192 | 14 | - |